TECHNICAL CHARACTERISTICS OF THE PRODUCT
Two-component polyurethane white enamel
Component А: BLICK WOOD ENAMEL PU 710 White 100% Gloss
Component В: BLICK WOOD HARDENER ENAMEL PU 710
Component С: BLICK WOOD THINNER 476
|
| Gloss |
100% gloss |
| Color |
White, opaque, pigmented enamel (any color is possible according to the RAL tone card or according to the sample).
|
|
Properties
|
This product has excellent coverage and thixotropic properties, uniformity of white coating, excellent filling, high hardness, fast drying time, good chemical and mechanical resistance, strength and elasticity. Resistance to UV radiation, does not turn yellow over time.
|
Application
|
Finishing polyurethane two-component coating for application on wood, furniture parts made of MDF and chipboard, massif, veneer, flat and curved surfaces made of wood.
During the process of the products, it is recommended to first use primer Blick Wood PRIMING FILLER 230 White
|
Surface preparation
|
The surface must be polished with abrasive materials P 320-400, and also cleaned of dust.
|
|
Mixture preparation
|
The products must be thoroughly mixed before starting work
|
|
Component А:
Component В:
Component С: |
Вy volume, %
|
Вy weight, %
|
|
100
50
40-50
|
100
40
40-50
|
|
Application method
|
Manual and automatic spraying is possible. The primer is applied with a pneumatic gun with a nozzle of 1.5- 1.7 mm and an air pressure of 3 atm. It is possible to apply with the help of convective spraying (airless) or with the help of airmix equipment.
|
Consumption
|
120-180 g/m2 for one layer.
|
CHEMICAL AND PHYSICAL CHARACTERISTICS OF THE PRODUCT
|
|
Viscosity (VZ-4 4mm), s
|
Component А: 430-480
Component В: 12-15
|
Dry residue, %
|
Component А: 75-78
Component В: 35-40
Component А+В: 68-70
|
Density, g/ml
|
Component А: 1,30±0,03
Component В: 1,05±0,03
Component С: 0,87±0,03
|
|
Pot life (А+В)
|
6 hours
|
|
Drying time of coating for 1 layer at 20ºС
|
Dust resistance: 15 min.
Peel resistance: 45 minutes.
Suitability for grinding: 8 hours.
(Recommended after 24 hours after complete drying).
|
|
Storage terms and conditions
|
Base (Component A) and hardener (Component B) in closed original packaging at a temperature of 15-25ºС - 12 months.
|