TECHNICAL CHARACTERISTICS OF THE PRODUCT
Two-component polyurethane lacquer
Component А: BLICK WOOD CLEAR COAT PU 870 PREMIUM 100% Gloss
Component В: BLICK WOOD HARDENER CLEAR COAT PU 870 PREMIUM
Component С: BLICK WOOD THINNER 476
|
| Gloss |
100% gloss |
| Color |
Perfectly transparent suspension
|
|
Properties
|
This product has perfect clarity, high hardness, fast drying time, good chemical resistance, strength and elasticity, and high dry residue. It is ideal as a protective coating on Blick Wood polyurethane enamels. It is resistant to ultraviolet radiation, it does not turn yellow over time.
|
Application
|
Universal high-gloss lacquer for application on wood and MDF (furniture, facades, parquet, countertops, etc.). During the process of the products made of natural wood or veneer, it is recommended to first use polyurethane primer Blick Wood PRIMING FILLER PU 220 Transparent.
|
Surface preparation
|
The surface must be polished with abrasive materials P 150-320, and also cleaned of dust.
|
|
Mixture preparation
|
The products must be thoroughly mixed before starting work
|
|
Component А:
Component В:
Component С: |
Вy volume, %
|
Вy weight, %
|
|
100
50
30-40
|
100
54
30-40
|
|
Application method
|
Manual and automatic spraying is possible. The primer is applied with a pneumatic gun with a nozzle of 1.5 mm and an air pressure of 3 atm. It is possible to apply with the help of convective spraying (airless) or with the help of airmix equipment.
|
Consumption
|
120-150 g/m2 for one layer.
|
CHEMICAL AND PHYSICAL CHARACTERISTICS OF THE PRODUCT
|
|
Viscosity (VZ-4 4mm), s
|
Component А: 100-120
Component В: 12-15
|
Dry residue, %
|
Component А: 50-55
Component В: 43-48
Component А+В: 50-52
|
Density, g/ml
|
Component А: 1,00±0,03
Component В: 1,07±0,03
Component С: 0,87±0,03
|
|
Pot life (А+В)
|
6 hours
|
|
Drying time of coating for 1 layer at 20ºС
|
Dust resistance: 30 min.
Peel resistance: 1 hour.
Suitability for grinding: 8 hours.
(Recommended after 24 hours after complete drying).
|
|
Storage terms and conditions
|
Base (Component A) and hardener (Component B) in closed original packaging at a temperature of 15-25ºС - 12 months.
|