TECHNICAL CHARACTERISTICS OF THE PRODUCT
Two-component polyurethane lacquer
Component А: BLICK WOOD CLEAR COAT PU 870 100% Gloss
Component В: BLICK WOOD HARDENER CLEAR COAT PU 870
Component С: BLICK WOOD THINNER 476
|
| Gloss |
100% gloss |
| Color |
Perfectly transparent suspension
|
|
Properties
|
This product has perfect transparency, high hardness, fast drying time, good chemical resistance, strength, elasticity and practically, does not change the color of the precoat layer. It is ideal for a protective layer on polyurethane enamels. It is resistant to ultraviolet radiation, does not turn yellow.
|
Application
|
Universal high-gloss lacquer for application on wood and MDF (furniture, facades, parquet, countertops, etc.). During the process of the products made of natural wood or veneer, it is recommended to first use polyurethane primer Blick Wood PRIMING FILLER PU 220 Transparent.
|
Surface preparation
|
The surface must be polished with abrasive materials P 150-320, and also cleaned of dust.
|
|
Mixture preparation
|
The products must be thoroughly mixed before starting work
|
|
Component А:
Component В:
Component С: |
Вy volume, %
|
Вy weight, %
|
|
100
50
10-15
|
100
53
10-15
|
|
Application method
|
Manual and automatic spraying is possible. The primer is applied with a pneumatic gun with a nozzle of 1.5 mm and an air pressure of 3 atm. It is possible to apply with the help of convective spraying (airless) or with the help of airmix equipment.
|
Consumption
|
120-150 g/m2 for one layer.
|
CHEMICAL AND PHYSICAL CHARACTERISTICS OF THE PRODUCT
|
|
Viscosity (VZ-4 4mm), s
|
Component А: 30-35
Component В: 11-14
|
Dry residue, %
|
Component А: 45-50
Component В: 40-45
Component А+В: 44-48
|
Density, g/ml
|
Component А: 0,99±0,03
Component В: 1,05±0,03
Component С: 0,87±0,03
|
|
Pot life (А+В)
|
6 hours
|
|
Drying time of coating for 1 layer at 20ºС
|
Dust resistance: 30 min.
Peel resistance: 1 hour.
Suitability for grinding: 8 hours.
(Recommended after 24 hours after complete drying).
|
|
Storage terms and conditions
|
Base (Component A) and hardener (Component B) in closed original packaging at a temperature of 15-25ºС - 12 months.
|