BLICK WOOD ENAMEL PU 710

TECHNICAL CHARACTERISTICS OF THE PRODUCT Two-component polyurethane white enamel Component А: BLICK WOOD ENAMEL PU 710 White 100% Gloss Component В: BLICK WOOD HARDENER ENAMEL PU 710 Component С: BLICK WOOD THINNER 476
Gloss	100% gloss
Color	White, opaque, pigmented enamel (any color is possible according to the RAL tone card or according to the sample).
Properties	This product has excellent coverage and thixotropic properties, uniformity of white coating, excellent filling, high hardness, fast drying time, good chemical and mechanical resistance, strength and elasticity. Resistance to UV radiation, does not turn yellow over time.
Application	Finishing polyurethane two-component coating for application on wood, furniture parts made of MDF and chipboard, massif, veneer, flat and curved surfaces made of wood. During the process of the products, it is recommended to first use primer Blick Wood PRIMING FILLER 230 White
Surface preparation	The surface must be polished with abrasive materials P 320-400, and also cleaned of dust.
Mixture preparation	The products must be thoroughly mixed before starting work
	Component А: Component В: Component С:	Вy volume, %	Вy weight, %
		100 50 40-50	100 40 40-50
Application method	Manual and automatic spraying is possible. The primer is applied with a pneumatic gun with a nozzle of 1.5- 1.7 mm and an air pressure of 3 atm. It is possible to apply with the help of convective spraying (airless) or with the help of airmix equipment.
Consumption	120-180 g/m2 for one layer.
CHEMICAL AND PHYSICAL CHARACTERISTICS OF THE PRODUCT
Viscosity (VZ-4 4mm), s	Component А: 430-480 Component В: 12-15
Dry residue, %	Component А: 75-78 Component В: 35-40 Component А+В: 68-70
Density, g/ml	Component А: 1,30±0,03 Component В: 1,05±0,03 Component С: 0,87±0,03
Pot life (А+В)	6 hours
Drying time of coating for 1 layer at 20ºС	Dust resistance: 15 min. Peel resistance: 45 minutes. Suitability for grinding: 8 hours. (Recommended after 24 hours after complete drying).
Storage terms and conditions	Base (Component A) and hardener (Component B) in closed original packaging at a temperature of 15-25ºС - 12 months.