BLICK WOOD PRIMING FILLER PU 230

Print page

TECHNICAL CHARACTERISTICS OF THE PRODUCT

White two-component polyurethane primer

Component А: BLICK WOOD PRIMING FILLER PU 230 White

Component В: BLICK WOOD HARDENER PRIMING FILLER PU 230

Component С: BLICK WOOD THINNER 723

Color White, opaque, pigmented

Properties

This product has excellent coverage and thixotropic properties, excellent fill, fast drying time and is easy to sand.
Application

Two-component polyurethane white primer for application on wood, furniture parts made of MDF and chipboard, massif, veneer, flat and curved surfaces made of wood. It is an ideal primer for the subsequent application of a glossy finish coating.
During the process of the products, it is recommended to first use polyurethane primer (insulator) Blick Wood PRIMING FILLER 220 Transparent.

Surface preparation
The surface must be polished with abrasive materials P 150-240, and also cleaned of dust.

Mixture preparation 

The products must be thoroughly mixed before starting work

 

 

Component А: 

Component В: 

Component С:

Вy volume, %

Вy weight, %

100

30

10-20 

100

20

10-20 

Application method

Manual and automatic spraying is possible. The primer is applied with a pneumatic gun with a nozzle of 1.7 mm and an air pressure of 3 atm. It is possible to apply with the help of convective spraying (airless) or with the help of airmix equipment.

Consumption
150-250 g/m2 for one layer.
CHEMICAL AND PHYSICAL CHARACTERISTICS OF THE PRODUCT

Viscosity (VZ-4 4mm), s

Component А: thixotropic

Component В: 12-15 

Brookfield viscosity at 230C (R4/4), mPa*s

Component А: 30 000 - 40 000

Dry residue, %

Component А: 75-80

Component В: 35-40 

Component А+В: 70-72

Density, g/ml

Component А: 1,70±0,03

Component В: 1,05±0,03

Component С: 0,85±0,03

Pot life (А+В)

3-4 hours

Drying time of coating for 1 layer at 20ºС

Dust resistance: 10 min.
Peel resistance: 30 minutes.
Suitability for grinding: 4 hours.
(Recommended after 24 hours after complete drying).

Storage terms and conditions 

Base (Component A) and hardener (Component B) in closed original packaging at a temperature of 15-25ºС - 12 months. 