Two-component thin-layer coldspray plastic for manual application
|PROPERTIES||System (A+B) with mixing ratio 98% +2%, which components are supplied separately and mixed immediatelybefore application. The catalystis added to the component B. Components A+Bare mixed outside immediately prior to applicationand coating rapidly hardens.
|AREA OF APPLICATION
||It has been designed for permanent road marking ofpedestrian crossings, cycle lanes, stop lines, arrows,safety island, pictograms and etc., for roads coveredwith asphalt and concrete, with service life more thantwo years.
||It is applied with specialized high pressure airless pumps.Separate pumps are used for components A and B, one forcomponent A, another for component B in which catalystis added. Components A+B are mixed immediately whenspraying outside of two-way spray gun. Depending onthe outside temperature add 1 to 2% catalyst.
||between 0,85 to 2,1 kg/m2 at a layer thickness of 0,6-1,1 mm
||Mechanically resilient, flexible, 100% adhesion to surface, free of solvents, UV, IR- resistant, fast curing, alkali-resistant
||(A+B+C) with mixing ratio 50%+48%+2%, between 4 to 10 minutes at +20°С|
||Before applying remove the traces of the previousmarking. Surface must be clean, dry, free of dust, earth,mud, salt, oil and other dirt. On the concrete, apply aprimer Signakul PCP 01. Environmental temperature at application must be between +5°С and +35°С. Substrate temperature must not be below 0°С and over +40°С. Environmental temperature at application must be Relative humidity must not exceed 85%.
||CP 25-10-25 comp. A - metal can -25 kg, CP 25-20-25 comp. B. Catalyst comp. C: зowdered – 0,5 - 25 kgб дiquid – 0,5 - 22,5 kg
||12 months if it is kept at a temperature of at least +5°С and a maximum of +25°С in original sealed packaging.
||When handling it is necessary to strictly follow safety procedures and fire protection measures which are contained in the standards and technical documentation of the product.