Two-component cold plastic forthick-layer agglomerate line roadmarking with anti-skid effect
| PROPERTIES | System (A+B) with mixing ratio 98% +2%, which components are supplied separately and mixed immediatelybefore application. The mixed components remain thixotropic fluid prior to application and then rapidly harden through chemical reaction which is strongly influenced by the air and temperature of the application surface. |
| AREA OF APPLICATION |
It has been designed for permanent road marking of longitudial agglomerate line. It is applied for highways and streets covered with asphalt and concrete with service lifemore than four years. |
| APPLICATION CONDITIONS |
It is applied with specialized two-component markingmachines by extrusion or screed box method withthe use of needle shaft. Depending on the outsidetemperature add 1 to 2% catalyst. |
| CONSUMPTION |
4-5 kg/m2 at a layer thickness of 2-3 mm |
| CHARACTERISTICS |
Mechanically resilient, flexible, 100% adhesion to surface, free of solvents, UV, IR- resistant, fast curing, alkali-resistant |
| COLOR |
White |
| DENSITY |
within 1,86-1,95 g/cm3 |
| SOLIDS CONTENT |
>99% |
| HARDENING TIME |
(A + B) with mixing ratio 98% + 2%, approx. 12 to 20 minutes at +20°С |
| APPLICATION METHOD |
Before applying remove the traces of the previousmarking. Surface must be clean, dry, free of dust, earth,mud, salt, oil and other dirt. On the concrete, apply aprimer Signakul PCP 01. Environmental temperature at application must be between +5°С and +35°С. Substrate temperature must not be below 0°С and over +40°С. Environmental temperature at application must be Relative humidity must not exceed 85%. |
| PACKAGING |
Metal can -30 kg, catalyst: powdered - 25 kg; liquid - 20 kg; 22,5 kg |
| STORAGE |
12 months if it is kept at a temperature of at least +5°С and a maximum of +25°С in original sealed packaging. |
| SAFETY |
When handling it is necessary to strictly follow safety procedures and fire protection measures which are contained in the standards and technical documentation of the product. |